Steel 12CrMo4 +C vs 12CrMo4 +NT
Steel · 12CrMo4 temper comparison
12CrMo4 +C and 12CrMo4 +NT are two conditions of the same steel grade, 12CrMo4: +C (cold drawn) versus +NT (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. 12CrMo4 +C is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 330 MPa (47.9 ksi) for 12CrMo4 +NT, about 58% more; tensile strength follows at 620 MPa (89.9 ksi) vs 490 MPa (71.1 ksi). In exchange, 12CrMo4 +NT is the more ductile: elongation 25% versus 12% for 12CrMo4 +C, and 12CrMo4 +C is harder (195 HB vs 148 HB). 12CrMo4 +NT runs hotter in service (530°C vs 400°C continuous).
12CrMo4 +CChoose it when strength drives the design.
12CrMo4 +NTChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
12CrMo4 +C vs 12CrMo4 +NT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 29 MJ/kg12,468 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
12CrMo4 +C vs 12CrMo4 +NT — frequently asked
Is 12CrMo4 +C stronger than 12CrMo4 +NT?
Yes. 12CrMo4 +C has a typical yield strength of 520 MPa (75.4 ksi) against 330 MPa (47.9 ksi) for 12CrMo4 +NT — about 58% more. Tensile strength is 620 MPa (89.9 ksi) vs 490 MPa (71.1 ksi).
Which condition does FabDigit quote by default, +C or +NT?
+N is the default 12CrMo4 condition in the FabDigit quote flow (neither +C nor +NT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 12CrMo4 +C or 12CrMo4 +NT?
12CrMo4 +C, by a small margin. Both rate good for machinability — 63/100 against 58/100 for 12CrMo4 +NT; for welding the order is 12CrMo4 +NT first (very good, 70/100) then 12CrMo4 +C (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 12CrMo4 +C and 12CrMo4 +NT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.