Steel 1211-ANN vs 1211-HR
Steel · 1211 temper comparison
1211-ANN and 1211-HR are two conditions of the same steel grade, 1211: ANN (annealed) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 1211-ANN is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 230 MPa (33.4 ksi) for 1211-HR, about 9% more. 1211-ANN is the more ductile: elongation 28% versus 25% for 1211-HR, and 1211-ANN is harder (171 HV vs 127 HV). 1211-HR runs hotter in service (400°C vs 350°C continuous).
1211-ANNChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1211-HRChoose it when the part sees heat.
1211-ANN vs 1211-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29 · Compressive Strength 470 MPa68.2 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.87 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 51 W/m·K29.5 BTU/hr·ft·°F · Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 8 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Brazeability / Solderability 55 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1211-ANN vs 1211-HR — frequently asked
Is 1211-ANN stronger than 1211-HR?
Yes. 1211-ANN has a typical yield strength of 250 MPa (36.3 ksi) against 230 MPa (33.4 ksi) for 1211-HR — about 9% more. Tensile strength is 395 MPa (57.3 ksi) vs 380 MPa (55.1 ksi).
Which condition does FabDigit quote by default, ANN or HR?
CD is the default 1211 condition in the FabDigit quote flow (neither ANN nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1211-ANN over 1211-HR?
Pick 1211-ANN when strength drives the design, or when the part is bent, formed or impact-loaded. Pick 1211-HR when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1211-ANN and 1211-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.