Steel 11SMnPb30 Annealed vs 11SMnPb30-HR
Steel · 11SMnPb30 temper comparison
11SMnPb30 Annealed and 11SMnPb30-HR are two conditions of the same steel grade, 11SMnPb30: Annealed versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 11SMnPb30-HR is the stronger of the two: yield strength 260 MPa (37.7 ksi) against 240 MPa (34.8 ksi) for 11SMnPb30 Annealed, about 8% more; tensile strength follows at 480 MPa (69.6 ksi) vs 420 MPa (60.9 ksi). In exchange, 11SMnPb30 Annealed is the more ductile: elongation 25% versus 22% for 11SMnPb30-HR, and 11SMnPb30-HR is harder (135 HB vs 120 HB).
11SMnPb30 AnnealedChoose it when the part is bent, formed or impact-loaded.
11SMnPb30-HRChoose it when strength drives the design.
11SMnPb30 Annealed vs 11SMnPb30-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
11SMnPb30 Annealed11SMnPb30-HR
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Shear Strength 300 MPa43.5 ksi · Hardness, Vickers 180 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 48 W/m·K27.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 250°C482 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9.5 % IACS · Electrical Resistivity 1.8×10⁻⁷ Ω·m7.09 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 12 / 100 · Brazeability / Solderability 45 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
11SMnPb30 Annealed vs 11SMnPb30-HR — frequently asked
Is 11SMnPb30-HR stronger than 11SMnPb30 Annealed?
Yes. 11SMnPb30-HR has a typical yield strength of 260 MPa (37.7 ksi) against 240 MPa (34.8 ksi) for 11SMnPb30 Annealed — about 8% more. Tensile strength is 480 MPa (69.6 ksi) vs 420 MPa (60.9 ksi).
Which condition does FabDigit quote by default, Annealed or HR?
HR is the default 11SMnPb30 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 11SMnPb30 Annealed over 11SMnPb30-HR?
Pick 11SMnPb30 Annealed when the part is bent, formed or impact-loaded. Pick 11SMnPb30-HR when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 11SMnPb30 Annealed and 11SMnPb30-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.