Steel 1151-HR vs 1151-IH
Steel · 1151 temper comparison
1151-HR and 1151-IH are two conditions of the same steel grade, 1151: HR (hot rolled) versus IH (induction hardened). The chemistry is identical, so every difference below comes from the condition. 1151-IH is the stronger of the two: yield strength 640 MPa (92.8 ksi) against 360 MPa (52.2 ksi) for 1151-HR, about 78% more; tensile strength follows at 745 MPa (108 ksi) vs 655 MPa (95 ksi). In exchange, 1151-HR is the more ductile: elongation 15% versus 8% for 1151-IH, and 1151-IH is harder (615 HB vs 192 HB). 1151-HR runs hotter in service (400°C vs 200°C continuous) and 1151-HR conducts electricity better (9.5 % IACS vs 8.5 % IACS). On the shop floor, 1151-HR machines more easily (very good vs poor) and 1151-HR welds better (poor vs not recommended).
1151-HRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1151-IHChoose it when strength drives the design.
1151-HR vs 1151-IH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.65 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 55 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 50 L/kg6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1151-HR vs 1151-IH — frequently asked
Is 1151-IH stronger than 1151-HR?
Yes. 1151-IH has a typical yield strength of 640 MPa (92.8 ksi) against 360 MPa (52.2 ksi) for 1151-HR — about 78% more. Tensile strength is 745 MPa (108 ksi) vs 655 MPa (95 ksi).
Which condition does FabDigit quote by default, HR or IH?
CD is the default 1151 condition in the FabDigit quote flow (neither HR nor IH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1151-HR or 1151-IH?
1151-HR. Its machinability rates very good (70/100) against poor (20/100) for 1151-IH; for welding the order is 1151-HR first (poor, 20/100) then 1151-IH (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1151-HR and 1151-IH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.