Steel 10B22-N vs 10B22 QT-98
Steel · 10B22 temper comparison
10B22-N and 10B22 QT-98 are two conditions of the same steel grade, 10B22: N (normalized) versus QT-98. The chemistry is identical, so every difference below comes from the condition. 10B22 QT-98 is the stronger of the two: yield strength 780 MPa (113 ksi) against 345 MPa (50 ksi) for 10B22-N, about 126% more; tensile strength follows at 950 MPa (138 ksi) vs 510 MPa (74 ksi). In exchange, 10B22-N is the more ductile: elongation 26% versus 12% for 10B22 QT-98, and 10B22 QT-98 is harder (300 HB vs 150 HB). 10B22-N runs hotter in service (400°C vs 300°C continuous) and 10B22-N conducts electricity better (10.5 % IACS vs 9 % IACS). On the shop floor, 10B22-N machines more easily (good vs fair) and 10B22-N welds better (very good vs fair).
10B22-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
10B22 QT-98Choose it when strength drives the design.
10B22-N vs 10B22 QT-98: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 65 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
10B22-N vs 10B22 QT-98 — frequently asked
Is 10B22 QT-98 stronger than 10B22-N?
Yes. 10B22 QT-98 has a typical yield strength of 780 MPa (113 ksi) against 345 MPa (50 ksi) for 10B22-N — about 126% more. Tensile strength is 950 MPa (138 ksi) vs 510 MPa (74 ksi).
Which condition does FabDigit quote by default, N or QT-98?
CD is the default 10B22 condition in the FabDigit quote flow (neither N nor QT-98). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 10B22-N or 10B22 QT-98?
10B22-N. Its machinability rates good (58/100) against fair (42/100) for 10B22 QT-98; for welding the order is 10B22-N first (very good, 72/100) then 10B22 QT-98 (fair, 48/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 10B22-N and 10B22 QT-98 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.