Steel 1084 vs 1086
Steel · grade comparison
Steel 1084 and 1086 are both steel grades. 1084 is the stronger of the two: yield strength 585 MPa (84.8 ksi) against 540 MPa (78.3 ksi) for 1086, about 8% more. 1084 is harder — 293 HB against 269 HB for 1086 — which matters for wear surfaces and threads. On the shop floor, 1086 sits in a lower cost tier (budget, $) than 1084 (standard, $$).
1084Choose it when strength drives the design, or when surface hardness matters.
1086Choose it when cost is the deciding factor.
1084 vs 1086: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 12% · Fatigue Strength (Endurance Limit) 420 MPa60.9 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9.6 % IACS · Electrical Resistivity 1.8×10⁻⁷ Ω·m7.09 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 45% · Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1084 | 1086 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
1084 vs 1086 — frequently asked
Is 1084 stronger than 1086?
Yes. 1084 has a typical yield strength of 585 MPa (84.8 ksi) against 540 MPa (78.3 ksi) for 1086 — about 8% more. Tensile strength is 965 MPa (140 ksi) vs 930 MPa (135 ksi).
Which is cheaper, 1084 or 1086?
1086 is the lower-cost material: it sits in the budget tier ($) while 1084 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 1084 or 1086?
1084. Its weldability rates poor (20/100) against poor (15/100) for 1086.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1084 and 1086 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.