Steel 1060 vs 1084
Steel · grade comparison
Steel 1060 and 1084 are both steel grades, both high carbon steel. 1084 is the stronger of the two: yield strength 585 MPa (84.8 ksi) against 370 MPa (53.7 ksi) for 1060, about 58% more; tensile strength follows at 965 MPa (140 ksi) vs 675 MPa (97.9 ksi). In exchange, 1060 is the more ductile: elongation 17% versus 12% for 1084, and 1084 is harder (293 HB vs 201 HB). 1084 runs hotter in service (400°C vs 300°C continuous). On the shop floor, 1060 machines more easily (45 vs 35 out of 100).
1060Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
1084Choose it when strength drives the design, or when the part sees heat.
1060 vs 1084: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.3 µm/m·K6.3 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9.6 % IACS · Electrical Resistivity 1.8×10⁻⁷ Ω·m7.09 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 30 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1060 | 1084 |
|---|---|---|
| Default condition | HR | HR |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
1060 vs 1084 — frequently asked
Is 1084 stronger than 1060?
Yes. 1084 has a typical yield strength of 585 MPa (84.8 ksi) against 370 MPa (53.7 ksi) for 1060 — about 58% more. Tensile strength is 965 MPa (140 ksi) vs 675 MPa (97.9 ksi).
Which is cheaper, 1060 or 1084?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1060 or 1084?
1060, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 1084; for welding the order is 1060 first (poor, 25/100) then 1084 (poor, 20/100).