Steel 1010 vs C4C
Steel · grade comparison
Steel 1010 and C4C are both steel grades. C4C is the stronger of the two: yield strength 210 MPa (30.5 ksi) against 180 MPa (26.1 ksi) for 1010, about 17% more. C4C is the more ductile: elongation 38% versus 28% for 1010. C4C conducts heat better (58 W/m·K vs 49.8 W/m·K).
C4CChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1010 vs C4C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Compressive Strength
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 95 HB · Hardness, Rockwell B 55 HRB · Hardness, Vickers 100 HV
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.87 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Polishability
Same in both: Machinability 42 / 100 · Weldability 95 / 100 · Brazeability / Solderability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1010 | C4C |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
1010 vs C4C — frequently asked
Is C4C stronger than 1010?
Yes. C4C has a typical yield strength of 210 MPa (30.5 ksi) against 180 MPa (26.1 ksi) for 1010 — about 17% more. Tensile strength is 330 MPa (47.9 ksi) vs 325 MPa (47.1 ksi).
Which is cheaper, 1010 or C4C?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose 1010 over C4C?
Pick C4C when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1010 and C4C side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.