Steel 100CrMnSi6-6 +AC+SH vs 100CrMnSi6-6 +AR
Steel · 100CrMnSi6-6 temper comparison
100CrMnSi6-6 +AC+SH and 100CrMnSi6-6 +AR are two conditions of the same steel grade, 100CrMnSi6-6: +AC+SH (spheroidize annealed, peeled / turned-and-polished bar) versus +AR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 100CrMnSi6-6 +AR is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 410 MPa (59.5 ksi) for 100CrMnSi6-6 +AC+SH, about 51% more; tensile strength follows at 1,050 MPa (152 ksi) vs 680 MPa (98.6 ksi). In exchange, 100CrMnSi6-6 +AC+SH is the more ductile: elongation 22% versus 10% for 100CrMnSi6-6 +AR, and 100CrMnSi6-6 +AR is harder (290 HB vs 195 HB). On the shop floor, 100CrMnSi6-6 +AC+SH machines more easily (fair vs poor).
100CrMnSi6-6 +AC+SHChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
100CrMnSi6-6 +ARChoose it when strength drives the design.
100CrMnSi6-6 +AC+SH vs 100CrMnSi6-6 +AR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
100CrMnSi6-6 +AC+SH100CrMnSi6-6 +AR
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 700 MPa102 ksi · Shear Strength 420 MPa60.9 ksi · Fatigue Strength (Endurance Limit) 320 MPa46.4 ksi · Hardness, Rockwell B 92 HRB · Hardness, Vickers 205 HV
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 4.3 % IACS · Electrical Resistivity 4×10⁻⁷ Ω·m15.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
100CrMnSi6-6 +AC+SH vs 100CrMnSi6-6 +AR — frequently asked
Is 100CrMnSi6-6 +AR stronger than 100CrMnSi6-6 +AC+SH?
Yes. 100CrMnSi6-6 +AR has a typical yield strength of 620 MPa (89.9 ksi) against 410 MPa (59.5 ksi) for 100CrMnSi6-6 +AC+SH — about 51% more. Tensile strength is 1,050 MPa (152 ksi) vs 680 MPa (98.6 ksi).
Which condition does FabDigit quote by default, +AC+SH or +AR?
+AC is the default 100CrMnSi6-6 condition in the FabDigit quote flow (neither +AC+SH nor +AR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 100CrMnSi6-6 +AC+SH or 100CrMnSi6-6 +AR?
100CrMnSi6-6 +AC+SH. Its machinability rates fair (47/100) against poor (30/100) for 100CrMnSi6-6 +AR.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 100CrMnSi6-6 +AC+SH and 100CrMnSi6-6 +AR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.