Steel 1008-HR vs 1008 Normalized
Steel · 1008 temper comparison
1008-HR and 1008 Normalized are two conditions of the same steel grade, 1008: HR (hot rolled) versus Normalized. The chemistry is identical, so every difference below comes from the condition. 1008 Normalized is the stronger of the two: yield strength 195 MPa (28.3 ksi) against 175 MPa (25.4 ksi) for 1008-HR, about 11% more; tensile strength follows at 325 MPa (47.1 ksi) vs 300 MPa (43.5 ksi). 1008 Normalized is harder — 50 HRB against 45 HRB for 1008-HR — which matters for wear surfaces and threads.
1008 NormalizedChoose it when strength drives the design, or when surface hardness matters.
1008-HR vs 1008 Normalized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.87 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 60 W/m·K34.7 BTU/hr·ft·°F · Specific Heat Capacity 481 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 425°C797 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11.5 % IACS · Electrical Resistivity 1.5×10⁻⁷ Ω·m5.91 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.65 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 95 / 100 · Brazeability / Solderability 80 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1008-HR vs 1008 Normalized — frequently asked
Is 1008 Normalized stronger than 1008-HR?
Yes. 1008 Normalized has a typical yield strength of 195 MPa (28.3 ksi) against 175 MPa (25.4 ksi) for 1008-HR — about 11% more. Tensile strength is 325 MPa (47.1 ksi) vs 300 MPa (43.5 ksi).
Which condition does FabDigit quote by default, HR or Normalized?
HR is the default 1008 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1008-HR over 1008 Normalized?
Pick 1008 Normalized when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1008-HR and 1008 Normalized side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.