Steel 1.2363 Annealed vs 1.2363 HT 60-62 HRC
Steel · 1.2363 temper comparison
1.2363 Annealed and 1.2363 HT 60-62 HRC are two conditions of the same steel grade, 1.2363: Annealed versus HT 60-62 HRC (hardened + tempered 175–200 °C). The chemistry is identical, so every difference below comes from the condition. 1.2363 HT 60-62 HRC is the stronger of the two: yield strength 1,900 MPa (276 ksi) against 500 MPa (72.5 ksi) for 1.2363 Annealed, about 3.8 times as much; tensile strength follows at 2,200 MPa (319 ksi) vs 790 MPa (115 ksi). In exchange, 1.2363 Annealed is the more ductile: elongation 16% versus 1% for 1.2363 HT 60-62 HRC, and 1.2363 HT 60-62 HRC is harder (720 HV vs 230 HV). 1.2363 Annealed runs hotter in service (400°C vs 180°C continuous). On the shop floor, 1.2363 Annealed machines more easily (fair vs not recommended).
1.2363 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.2363 HT 60-62 HRCChoose it when strength drives the design.
1.2363 Annealed vs 1.2363 HT 60-62 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
1.2363 Annealed1.2363 HT 60-62 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Reduction in Area 35% · Hardness, Brinell 220 HB · Hardness, Rockwell B 97 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.86 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,460°C2,660 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11 µm/m·K6.1 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.7 % IACS · Electrical Resistivity 6.5×10⁻⁷ Ω·m25.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 18 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Polishability
Same in both: Weldability 20 / 100 · Formability (cold) 15 / 100 · Brazeability / Solderability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 33 MJ/kg14,187 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.2363 Annealed vs 1.2363 HT 60-62 HRC — frequently asked
Is 1.2363 HT 60-62 HRC stronger than 1.2363 Annealed?
Yes. 1.2363 HT 60-62 HRC has a typical yield strength of 1,900 MPa (276 ksi) against 500 MPa (72.5 ksi) for 1.2363 Annealed — about 3.8 times as much. Tensile strength is 2,200 MPa (319 ksi) vs 790 MPa (115 ksi).
Which condition does FabDigit quote by default, Annealed or HT 60-62 HRC?
Annealed is the default 1.2363 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.2363 Annealed or 1.2363 HT 60-62 HRC?
1.2363 Annealed. Its machinability rates fair (40/100) against not recommended (8/100) for 1.2363 HT 60-62 HRC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.2363 Annealed and 1.2363 HT 60-62 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.