Steel 09CuPCrNi-CR vs 09CuPCrNi-N
Steel · 09CuPCrNi temper comparison
09CuPCrNi-CR and 09CuPCrNi-N are two conditions of the same steel grade, 09CuPCrNi: CR (cold rolled) versus N (normalized). The chemistry is identical, so every difference below comes from the condition. 09CuPCrNi-CR is the stronger of the two: yield strength 400 MPa (58 ksi) against 315 MPa (45.7 ksi) for 09CuPCrNi-N, about 27% more; tensile strength follows at 520 MPa (75.4 ksi) vs 460 MPa (66.7 ksi). In exchange, 09CuPCrNi-N is the more ductile: elongation 33% versus 22% for 09CuPCrNi-CR, and 09CuPCrNi-CR is harder (160 HB vs 140 HB). 09CuPCrNi-N runs hotter in service (350°C vs 300°C continuous).
09CuPCrNi-CRChoose it when strength drives the design.
09CuPCrNi-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
09CuPCrNi-CR vs 09CuPCrNi-N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 48 W/m·K27.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.6 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 50 L/kg6 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
09CuPCrNi-CR vs 09CuPCrNi-N — frequently asked
Is 09CuPCrNi-CR stronger than 09CuPCrNi-N?
Yes. 09CuPCrNi-CR has a typical yield strength of 400 MPa (58 ksi) against 315 MPa (45.7 ksi) for 09CuPCrNi-N — about 27% more. Tensile strength is 520 MPa (75.4 ksi) vs 460 MPa (66.7 ksi).
Which condition does FabDigit quote by default, CR or N?
HR is the default 09CuPCrNi condition in the FabDigit quote flow (neither CR nor N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 09CuPCrNi-CR over 09CuPCrNi-N?
Pick 09CuPCrNi-CR when strength drives the design. Pick 09CuPCrNi-N when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 09CuPCrNi-CR and 09CuPCrNi-N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.