Stainless Steel X20Cr13 +C vs X20Cr13 H+T350
Stainless Steel · X20Cr13 temper comparison
X20Cr13 +C and X20Cr13 H+T350 are two conditions of the same stainless steel grade, X20Cr13: +C (cold drawn) versus H+T350 (hardened ~1000 °C, tempered ~350 °C). The chemistry is identical, so every difference below comes from the condition. X20Cr13 H+T350 is the stronger of the two: yield strength 1,200 MPa (174 ksi) against 640 MPa (92.8 ksi) for X20Cr13 +C, about 88% more; tensile strength follows at 1,450 MPa (210 ksi) vs 820 MPa (119 ksi). In exchange, X20Cr13 +C is the more ductile: elongation 12% versus 8% for X20Cr13 H+T350, and X20Cr13 H+T350 is harder (420 HB vs 250 HB). X20Cr13 +C runs hotter in service (400°C vs 300°C continuous). On the shop floor, X20Cr13 +C machines more easily (good vs poor).
X20Cr13 +CChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
X20Cr13 H+T350Choose it when strength drives the design.
X20Cr13 +C vs X20Cr13 H+T350: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.5×10⁻⁷ Ω·m21.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
X20Cr13 +C vs X20Cr13 H+T350 — frequently asked
Is X20Cr13 H+T350 stronger than X20Cr13 +C?
Yes. X20Cr13 H+T350 has a typical yield strength of 1,200 MPa (174 ksi) against 640 MPa (92.8 ksi) for X20Cr13 +C — about 88% more. Tensile strength is 1,450 MPa (210 ksi) vs 820 MPa (119 ksi).
Which condition does FabDigit quote by default, +C or H+T350?
+A is the default X20Cr13 condition in the FabDigit quote flow (neither +C nor H+T350). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, X20Cr13 +C or X20Cr13 H+T350?
X20Cr13 +C. Its machinability rates good (58/100) against poor (28/100) for X20Cr13 H+T350; for welding the order is X20Cr13 H+T350 first (poor, 30/100) then X20Cr13 +C (poor, 25/100).