Stainless Steel SUS836L 1/4H vs SUS836L-AW
Stainless Steel · SUS836L temper comparison
SUS836L 1/4H and SUS836L-AW are two conditions of the same stainless steel grade, SUS836L: 1/4H (quarter hard) versus AW (as-welded deposit). The chemistry is identical, so every difference below comes from the condition. SUS836L 1/4H is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 330 MPa (47.9 ksi) for SUS836L-AW, about 67% more; tensile strength follows at 830 MPa (120 ksi) vs 620 MPa (89.9 ksi). In exchange, SUS836L-AW is the more ductile: elongation 35% versus 25% for SUS836L 1/4H, and SUS836L 1/4H is harder (238 HB vs 190 HB). SUS836L-AW runs hotter in service (400°C vs 350°C continuous).
SUS836L 1/4HChoose it when strength drives the design.
SUS836L-AWChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SUS836L 1/4H vs SUS836L-AW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 152 GPa22 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,320°C2,408 °F · Liquidus Temperature 1,390°C2,534 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 12 W/m·K6.9 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15.5 µm/m·K8.6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.8 % IACS · Electrical Resistivity 9.5×10⁻⁷ Ω·m37.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 75 MJ/kg32,244 BTU/lb · Embodied Carbon (primary production) 5.6 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SUS836L 1/4H vs SUS836L-AW — frequently asked
Is SUS836L 1/4H stronger than SUS836L-AW?
Yes. SUS836L 1/4H has a typical yield strength of 550 MPa (79.8 ksi) against 330 MPa (47.9 ksi) for SUS836L-AW — about 67% more. Tensile strength is 830 MPa (120 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, 1/4H or AW?
SA is the default SUS836L condition in the FabDigit quote flow (neither 1/4H nor AW). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SUS836L 1/4H or SUS836L-AW?
SUS836L 1/4H, by a small margin. Both rate poor for machinability — 30/100 against 24/100 for SUS836L-AW; for welding the order is SUS836L-AW first (very good, 70/100) then SUS836L 1/4H (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in SUS836L 1/4H and SUS836L-AW side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.