Stainless Steel S82011 1/4H vs S82011 Annealed
Stainless Steel · S82011 temper comparison
S82011 1/4H and S82011 Annealed are two conditions of the same stainless steel grade, S82011: 1/4H (quarter hard) versus Annealed. The chemistry is identical, so every difference below comes from the condition. S82011 1/4H is the stronger of the two: yield strength 750 MPa (109 ksi) against 520 MPa (75.4 ksi) for S82011 Annealed, about 44% more; tensile strength follows at 900 MPa (131 ksi) vs 700 MPa (102 ksi). In exchange, S82011 Annealed is the more ductile: elongation 32% versus 12% for S82011 1/4H, and S82011 1/4H is harder (290 HB vs 230 HB).
S82011 1/4HChoose it when strength drives the design.
S82011 AnnealedChoose it when the part is bent, formed or impact-loaded.
S82011 1/4H vs S82011 Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13 µm/m·K7.2 µin/in·°F · Latent Heat of Fusion 280 J/g120 BTU/lb · Max Service Temperature (continuous) 280°C536 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S82011 1/4H vs S82011 Annealed — frequently asked
Is S82011 1/4H stronger than S82011 Annealed?
Yes. S82011 1/4H has a typical yield strength of 750 MPa (109 ksi) against 520 MPa (75.4 ksi) for S82011 Annealed — about 44% more. Tensile strength is 900 MPa (131 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, 1/4H or Annealed?
Annealed is the default S82011 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, S82011 1/4H or S82011 Annealed?
S82011 Annealed. Its weldability rates very good (70/100) against good (64/100) for S82011 1/4H.