Stainless Steel S45503-H1000 vs S45503-H900
Stainless Steel · S45503 temper comparison
S45503-H1000 and S45503-H900 are two conditions of the same stainless steel grade, S45503: H1000 (aged 4 h at 538 °C (1000 °F), air cool) versus H900 (aged 482 °C (900 °F) for 1 h, peak hardness). The chemistry is identical, so every difference below comes from the condition. S45503-H900 is the stronger of the two: yield strength 1,620 MPa (235 ksi) against 1,450 MPa (210 ksi) for S45503-H1000, about 12% more; tensile strength follows at 1,720 MPa (249 ksi) vs 1,520 MPa (220 ksi). In exchange, S45503-H1000 is the more ductile: elongation 12% versus 10% for S45503-H900, and S45503-H900 is harder (477 HB vs 415 HB). S45503-H1000 runs hotter in service (425°C vs 350°C continuous). On the shop floor, S45503-H1000 welds better (good vs fair).
S45503-H1000Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S45503-H900Choose it when strength drives the design.
S45503-H1000 vs S45503-H900: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 159 GPa23.1 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.76 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,440°C2,624 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 17.9 W/m·K10.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.3 µm/m·K5.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 7.7×10⁻⁷ Ω·m30.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 20 / 100 · Brazeability / Solderability 40 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S45503-H1000 vs S45503-H900 — frequently asked
Is S45503-H900 stronger than S45503-H1000?
Yes. S45503-H900 has a typical yield strength of 1,620 MPa (235 ksi) against 1,450 MPa (210 ksi) for S45503-H1000 — about 12% more. Tensile strength is 1,720 MPa (249 ksi) vs 1,520 MPa (220 ksi).
Which condition does FabDigit quote by default, H1000 or H900?
H1000 is the default S45503 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S45503-H1000 or S45503-H900?
S45503-H1000, by a small margin. Both rate poor for machinability — 32/100 against 25/100 for S45503-H900; for welding the order is S45503-H1000 first (good, 55/100) then S45503-H900 (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in S45503-H1000 and S45503-H900 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.