Stainless Steel S44535-ANN vs S44535-TR
Stainless Steel · S44535 temper comparison
S44535-ANN and S44535-TR are two conditions of the same stainless steel grade, S44535: ANN (annealed) versus TR (temper rolled / skin passed). The chemistry is identical, so every difference below comes from the condition. S44535-TR is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 330 MPa (47.9 ksi) for S44535-ANN, about 15% more; tensile strength follows at 530 MPa (76.9 ksi) vs 500 MPa (72.5 ksi). In exchange, S44535-ANN is the more ductile: elongation 27% versus 22% for S44535-TR, and S44535-TR is harder (192 HB vs 180 HB).
S44535-ANNChoose it when the part is bent, formed or impact-loaded.
S44535-TRChoose it when strength drives the design.
S44535-ANN vs S44535-TR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.67 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 21 W/m·K12.1 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.7 % IACS · Electrical Resistivity 6.5×10⁻⁷ Ω·m25.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V · Corrosion Resistance 63 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 65 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 4.3 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 75%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S44535-ANN vs S44535-TR — frequently asked
Is S44535-TR stronger than S44535-ANN?
Yes. S44535-TR has a typical yield strength of 380 MPa (55.1 ksi) against 330 MPa (47.9 ksi) for S44535-ANN — about 15% more. Tensile strength is 530 MPa (76.9 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, ANN or TR?
ANN is the default S44535 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose S44535-ANN over S44535-TR?
Pick S44535-ANN when the part is bent, formed or impact-loaded. Pick S44535-TR when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in S44535-ANN and S44535-TR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.