Stainless Steel S31254 Annealed vs S31254 CW-1/2H
Stainless Steel · S31254 temper comparison
S31254 Annealed and S31254 CW-1/2H are two conditions of the same stainless steel grade, S31254: Annealed versus CW-1/2H (1/2 Hard). The chemistry is identical, so every difference below comes from the condition. S31254 CW-1/2H is the stronger of the two: yield strength 800 MPa (116 ksi) against 350 MPa (50.8 ksi) for S31254 Annealed, about 129% more; tensile strength follows at 1,000 MPa (145 ksi) vs 680 MPa (98.6 ksi). In exchange, S31254 Annealed is the more ductile: elongation 50% versus 10% for S31254 CW-1/2H, and S31254 CW-1/2H is harder (310 HB vs 200 HB). S31254 Annealed runs hotter in service (400°C vs 300°C continuous). On the shop floor, S31254 Annealed welds better (very good vs good).
S31254 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S31254 CW-1/2HChoose it when strength drives the design.
S31254 Annealed vs S31254 CW-1/2H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 162 GPa23.5 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,325°C2,417 °F · Liquidus Temperature 1,390°C2,534 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14 W/m·K8.1 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2 % IACS · Electrical Resistivity 8.5×10⁻⁷ Ω·m33.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 90 MJ/kg38,693 BTU/lb · Embodied Carbon (primary production) 6.2 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S31254 Annealed vs S31254 CW-1/2H — frequently asked
Is S31254 CW-1/2H stronger than S31254 Annealed?
Yes. S31254 CW-1/2H has a typical yield strength of 800 MPa (116 ksi) against 350 MPa (50.8 ksi) for S31254 Annealed — about 129% more. Tensile strength is 1,000 MPa (145 ksi) vs 680 MPa (98.6 ksi).
Which condition does FabDigit quote by default, Annealed or CW-1/2H?
Annealed is the default S31254 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S31254 Annealed or S31254 CW-1/2H?
S31254 Annealed, by a small margin. Both rate poor for machinability — 25/100 against 20/100 for S31254 CW-1/2H; for welding the order is S31254 Annealed first (very good, 70/100) then S31254 CW-1/2H (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in S31254 Annealed and S31254 CW-1/2H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.