Stainless Steel N08320 1/4H vs N08320 Annealed
Stainless Steel · N08320 temper comparison
N08320 1/4H and N08320 Annealed are two conditions of the same stainless steel grade, N08320: 1/4H (quarter hard) versus Annealed. The chemistry is identical, so every difference below comes from the condition. N08320 1/4H is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 265 MPa (38.4 ksi) for N08320 Annealed, about 134% more; tensile strength follows at 860 MPa (125 ksi) vs 585 MPa (84.8 ksi). In exchange, N08320 Annealed is the more ductile: elongation 45% versus 18% for N08320 1/4H, and N08320 1/4H is harder (240 HB vs 160 HB). N08320 Annealed runs hotter in service (500°C vs 300°C continuous).
N08320 1/4HChoose it when strength drives the design.
N08320 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
N08320 1/4H vs N08320 Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Shear Modulus 76 GPa11 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8.08 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11.5 W/m·K6.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.6 µm/m·K8.1 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.7 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.12 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 68 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 85 MJ/kg36,543 BTU/lb · Embodied Carbon (primary production) 6.2 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
N08320 1/4H vs N08320 Annealed — frequently asked
Is N08320 1/4H stronger than N08320 Annealed?
Yes. N08320 1/4H has a typical yield strength of 620 MPa (89.9 ksi) against 265 MPa (38.4 ksi) for N08320 Annealed — about 134% more. Tensile strength is 860 MPa (125 ksi) vs 585 MPa (84.8 ksi).
Which condition does FabDigit quote by default, 1/4H or Annealed?
Annealed is the default N08320 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, N08320 1/4H or N08320 Annealed?
N08320 Annealed, by a small margin. Both rate poor for machinability — 28/100 against 22/100 for N08320 1/4H; for welding the order is N08320 Annealed first (very good, 80/100) then N08320 1/4H (very good, 72/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in N08320 1/4H and N08320 Annealed side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.