Stainless Steel N08135-AW vs N08135-CW
Stainless Steel · N08135 temper comparison
N08135-AW and N08135-CW are two conditions of the same stainless steel grade, N08135: AW (as-welded deposit) versus CW (cold worked). The chemistry is identical, so every difference below comes from the condition. N08135-CW is the stronger of the two: yield strength 700 MPa (102 ksi) against 380 MPa (55.1 ksi) for N08135-AW, about 84% more; tensile strength follows at 900 MPa (131 ksi) vs 680 MPa (98.6 ksi). In exchange, N08135-AW is the more ductile: elongation 30% versus 22% for N08135-CW, and N08135-CW is harder (280 HB vs 205 HB).
N08135-AWChoose it when the part is bent, formed or impact-loaded.
N08135-CWChoose it when strength drives the design.
N08135-AW vs N08135-CW: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 162 GPa23.5 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,330°C2,426 °F · Liquidus Temperature 1,385°C2,525 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11.5 W/m·K6.6 BTU/hr·ft·°F · Specific Heat Capacity 450 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.5 µm/m·K8.1 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.6 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 90 MJ/kg38,693 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
N08135-AW vs N08135-CW — frequently asked
Is N08135-CW stronger than N08135-AW?
Yes. N08135-CW has a typical yield strength of 700 MPa (102 ksi) against 380 MPa (55.1 ksi) for N08135-AW — about 84% more. Tensile strength is 900 MPa (131 ksi) vs 680 MPa (98.6 ksi).
Which condition does FabDigit quote by default, AW or CW?
SA is the default N08135 condition in the FabDigit quote flow (neither AW nor CW). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, N08135-AW or N08135-CW?
N08135-CW, by a small margin. Both rate poor for machinability — 26/100 against 18/100 for N08135-AW; for welding the order is N08135-CW first (very good, 70/100) then N08135-AW (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in N08135-AW and N08135-CW side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.