Stainless Steel E630-A vs E630-H925
Stainless Steel · E630 temper comparison
E630-A and E630-H925 are two conditions of the same stainless steel grade, E630: A (solution annealed) versus H925 (aged 496 °C (925 °F) for 4 h). The chemistry is identical, so every difference below comes from the condition. E630-H925 is the stronger of the two: yield strength 1,100 MPa (160 ksi) against 760 MPa (110 ksi) for E630-A, about 45% more; tensile strength follows at 1,210 MPa (175 ksi) vs 1,030 MPa (149 ksi). In exchange, E630-A is the more ductile: elongation 12% versus 10% for E630-H925, and E630-H925 is harder (375 HB vs 311 HB). On the shop floor, E630-A machines more easily (fair vs poor) and E630-A welds better (very good vs good).
E630-AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
E630-H925Choose it when strength drives the design.
E630-A vs E630-H925: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 196 GPa28.4 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 142 GPa20.6 Msi · Poisson's Ratio 0.27
Physical
Density and transition temperatures.
Same in both: Density 7.78 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,404°C2,559 °F · Liquidus Temperature 1,440°C2,624 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 2.2 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
E630-A vs E630-H925 — frequently asked
Is E630-H925 stronger than E630-A?
Yes. E630-H925 has a typical yield strength of 1,100 MPa (160 ksi) against 760 MPa (110 ksi) for E630-A — about 45% more. Tensile strength is 1,210 MPa (175 ksi) vs 1,030 MPa (149 ksi).
Which condition does FabDigit quote by default, A or H925?
AW is the default E630 condition in the FabDigit quote flow (neither A nor H925). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, E630-A or E630-H925?
E630-A. Its machinability rates fair (42/100) against poor (28/100) for E630-H925; for welding the order is E630-A first (very good, 70/100) then E630-H925 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E630-A and E630-H925 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.