Stainless Steel CX As Printed vs CX Hardened & Tempered
Stainless Steel · CX temper comparison
CX As Printed and CX Hardened & Tempered are two conditions of the same stainless steel grade, CX: As Printed (as built (as printed)) versus Hardened & Tempered (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. CX Hardened & Tempered is the stronger of the two: yield strength 1,550 MPa (225 ksi) against 900 MPa (131 ksi) for CX As Printed, about 72% more; tensile strength follows at 1,670 MPa (242 ksi) vs 1,100 MPa (160 ksi). In exchange, CX As Printed is the more ductile: elongation 11% versus 5% for CX Hardened & Tempered, and CX Hardened & Tempered is harder (50 HRC vs 33 HRC). CX Hardened & Tempered is stiffer (200 GPa vs 185 GPa) and CX Hardened & Tempered runs hotter in service (400°C vs 350°C continuous). On the shop floor, CX As Printed machines more easily (fair vs poor).
CX As PrintedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
CX Hardened & TemperedChoose it when strength drives the design, or when the part sees heat.
CX As Printed vs CX Hardened & Tempered: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
CX As PrintedCX Hardened & Tempered
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 72 GPa10.4 Msi · Bulk Modulus 155 GPa22.5 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 310 HB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 18 W/m·K10.4 BTU/hr·ft·°F · Specific Heat Capacity 430 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.8 µm/m·K6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Polishability
Same in both: Weldability 70 / 100 · Formability (cold) 25 / 100 · Castability 45 / 100 · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 78 MJ/kg33,534 BTU/lb · Embodied Carbon (primary production) 6.8 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CX As Printed vs CX Hardened & Tempered — frequently asked
Is CX Hardened & Tempered stronger than CX As Printed?
Yes. CX Hardened & Tempered has a typical yield strength of 1,550 MPa (225 ksi) against 900 MPa (131 ksi) for CX As Printed — about 72% more. Tensile strength is 1,670 MPa (242 ksi) vs 1,100 MPa (160 ksi).
Which condition does FabDigit quote by default, As Printed or Hardened & Tempered?
As Printed is the default CX condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, CX As Printed or CX Hardened & Tempered?
CX As Printed. Its machinability rates fair (38/100) against poor (22/100) for CX Hardened & Tempered.