Stainless Steel CA6N-ANN vs CA6N N+T
Stainless Steel · CA6N temper comparison
CA6N-ANN and CA6N N+T are two conditions of the same stainless steel grade, CA6N: ANN (annealed) versus N+T (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. CA6N N+T is the stronger of the two: yield strength 930 MPa (135 ksi) against 560 MPa (81.2 ksi) for CA6N-ANN, about 66% more; tensile strength follows at 1,020 MPa (148 ksi) vs 760 MPa (110 ksi). In exchange, CA6N-ANN is the more ductile: elongation 24% versus 19% for CA6N N+T, and CA6N N+T is harder (300 HB vs 220 HB). On the shop floor, CA6N-ANN machines more easily (fair vs poor).
CA6N-ANNChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
CA6N N+TChoose it when strength drives the design.
CA6N-ANN vs CA6N N+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,465°C2,669 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.6 µm/m·K5.9 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 68 / 100 · Brazeability / Solderability 35 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 75%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CA6N-ANN vs CA6N N+T — frequently asked
Is CA6N N+T stronger than CA6N-ANN?
Yes. CA6N N+T has a typical yield strength of 930 MPa (135 ksi) against 560 MPa (81.2 ksi) for CA6N-ANN — about 66% more. Tensile strength is 1,020 MPa (148 ksi) vs 760 MPa (110 ksi).
Which condition does FabDigit quote by default, ANN or N+T?
N+T is the default CA6N condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, CA6N-ANN or CA6N N+T?
CA6N-ANN. Its machinability rates fair (48/100) against poor (32/100) for CA6N N+T; for welding the order is CA6N-ANN first (very good, 70/100) then CA6N N+T (good, 62/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in CA6N-ANN and CA6N N+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.