Stainless Steel Alloy 20 vs S31254
Stainless Steel · grade comparison
Stainless Steel Alloy 20 and S31254 are both stainless steel grades. S31254 is the stronger of the two: yield strength 350 MPa (50.8 ksi) against 310 MPa (45 ksi) for Alloy 20, about 13% more; tensile strength follows at 680 MPa (98.6 ksi) vs 620 MPa (89.9 ksi). S31254 is the more ductile: elongation 50% versus 40% for Alloy 20, and S31254 is harder (200 HB vs 160 HB). Alloy 20 runs hotter in service (500°C vs 400°C continuous) and S31254 conducts heat better (14 W/m·K vs 12 W/m·K). On the shop floor, Alloy 20 machines more easily (fair vs poor), Alloy 20 welds better (80 vs 70 out of 100), and S31254 sits in a lower cost tier (high, $$$$) than Alloy 20 (specialty, $$$$$).
Alloy 20Choose it when the part sees heat, or when the part is machined in volume.
S31254Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Alloy 20 vs S31254: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Hardness, Vickers
Same in both: Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 45%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Alloy 20 | S31254 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
Alloy 20 vs S31254 — frequently asked
Is S31254 stronger than Alloy 20?
Yes. S31254 has a typical yield strength of 350 MPa (50.8 ksi) against 310 MPa (45 ksi) for Alloy 20 — about 13% more. Tensile strength is 680 MPa (98.6 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, Alloy 20 or S31254?
S31254 is the lower-cost material: it sits in the high tier ($$$$) while Alloy 20 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Alloy 20 or S31254?
Alloy 20. Its machinability rates fair (38/100) against poor (25/100) for S31254; for welding the order is Alloy 20 first (very good, 80/100) then S31254 (very good, 70/100).