Stainless Steel 430 vs SUS430J1L
Stainless Steel · grade comparison
Stainless Steel 430 and SUS430J1L are both stainless steel grades. 430 is the stronger of the two: yield strength 310 MPa (45 ksi) against 290 MPa (42.1 ksi) for SUS430J1L, about 7% more; tensile strength follows at 500 MPa (72.5 ksi) vs 470 MPa (68.2 ksi). On the shop floor, SUS430J1L welds better (very good vs good) and SUS430J1L forms better (excellent vs good).
430Choose it when strength drives the design.
SUS430J1LChoose it when it will be welded.
430 vs SUS430J1L: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Fatigue Strength (Endurance Limit) 240 MPa34.8 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 26 W/m·K15 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Same in both: Specific Stiffness (E / density) 26 MN·m/kg · Thermal Diffusivity 7.3 mm²/s · Thermal Shock Resistance Index 6
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 430 | SUS430J1L |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
430 vs SUS430J1L — frequently asked
Is 430 stronger than SUS430J1L?
Yes. 430 has a typical yield strength of 310 MPa (45 ksi) against 290 MPa (42.1 ksi) for SUS430J1L — about 7% more. Tensile strength is 500 MPa (72.5 ksi) vs 470 MPa (68.2 ksi).
Which is cheaper, 430 or SUS430J1L?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 430 or SUS430J1L?
SUS430J1L. Its machinability rates good (55/100) against fair (50/100) for 430; for welding the order is SUS430J1L first (very good, 78/100) then 430 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 430 and SUS430J1L side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.