Stainless Steel 420J2 Annealed vs 420J2 Cold Drawn
Stainless Steel · 420J2 temper comparison
420J2 Annealed and 420J2 Cold Drawn are two conditions of the same stainless steel grade, 420J2: Annealed versus Cold Drawn. The chemistry is identical, so every difference below comes from the condition. 420J2 Cold Drawn is the stronger of the two: yield strength 700 MPa (102 ksi) against 400 MPa (58 ksi) for 420J2 Annealed, about 75% more; tensile strength follows at 850 MPa (123 ksi) vs 700 MPa (102 ksi). In exchange, 420J2 Annealed is the more ductile: elongation 20% versus 12% for 420J2 Cold Drawn, and 420J2 Cold Drawn is harder (265 HB vs 220 HB). 420J2 Annealed runs hotter in service (650°C vs 400°C continuous).
420J2 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
420J2 Cold DrawnChoose it when strength drives the design.
420J2 Annealed vs 420J2 Cold Drawn: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
420J2 Annealed420J2 Cold Drawn
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 50% · Compressive Strength 420 MPa60.9 ksi · Shear Strength 430 MPa62.4 ksi · Fatigue Strength (Endurance Limit) 340 MPa49.3 ksi · Hardness, Rockwell B 96 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24.9 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.5×10⁻⁷ Ω·m21.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V · Corrosion Resistance 40 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 25 / 100 · Brazeability / Solderability 40 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Carbon (primary production) 3.2 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
420J2 Annealed vs 420J2 Cold Drawn — frequently asked
Is 420J2 Cold Drawn stronger than 420J2 Annealed?
Yes. 420J2 Cold Drawn has a typical yield strength of 700 MPa (102 ksi) against 400 MPa (58 ksi) for 420J2 Annealed — about 75% more. Tensile strength is 850 MPa (123 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, Annealed or Cold Drawn?
Annealed is the default 420J2 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 420J2 Annealed over 420J2 Cold Drawn?
Pick 420J2 Annealed when the part is bent, formed or impact-loaded, or when the part sees heat. Pick 420J2 Cold Drawn when strength drives the design.