Stainless Steel 405 vs X2CrTi21
Stainless Steel · grade comparison
Stainless Steel 405 and X2CrTi21 are both stainless steel grades. X2CrTi21 is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 280 MPa (40.6 ksi) for 405, about 7% more. X2CrTi21 is harder — 170 HB against 155 HB for 405 — which matters for wear surfaces and threads. X2CrTi21 is stiffer (220 GPa vs 200 GPa) and X2CrTi21 runs hotter in service (950°C vs 705°C continuous). On the shop floor, X2CrTi21 forms better (very good vs good) and X2CrTi21 sits in a lower cost tier (standard, $$) than 405 (premium, $$$).
X2CrTi21Choose it when strength drives the design, or when surface hardness matters.
405 vs X2CrTi21: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Yield Strength (0.2% offset)
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Tensile Strength (Ultimate) 480 MPa69.6 ksi · Elongation at Break 28% · Reduction in Area 60% · Fatigue Strength (Endurance Limit) 240 MPa34.8 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Strength (UTS / density) 62 kN·m/kg
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 405 | X2CrTi21 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
405 vs X2CrTi21 — frequently asked
Is X2CrTi21 stronger than 405?
Yes. X2CrTi21 has a typical yield strength of 300 MPa (43.5 ksi) against 280 MPa (40.6 ksi) for 405 — about 7% more. Tensile strength is 480 MPa (69.6 ksi) vs 480 MPa (69.6 ksi).
Which is cheaper, 405 or X2CrTi21?
X2CrTi21 is the lower-cost material: it sits in the standard tier ($$) while 405 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 405 or X2CrTi21?
405. Its machinability rates good (55/100) against fair (50/100) for X2CrTi21; for welding the order is X2CrTi21 first (very good, 78/100) then 405 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 405 and X2CrTi21 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.