Stainless Steel 329 Annealed vs 329-CD
Stainless Steel · 329 temper comparison
329 Annealed and 329-CD are two conditions of the same stainless steel grade, 329: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 329-CD is the stronger of the two: yield strength 700 MPa (102 ksi) against 540 MPa (78.3 ksi) for 329 Annealed, about 30% more; tensile strength follows at 860 MPa (125 ksi) vs 720 MPa (104 ksi). In exchange, 329 Annealed is the more ductile: elongation 25% versus 16% for 329-CD, and 329-CD is harder (280 HB vs 230 HB).
329 AnnealedChoose it when the part is bent, formed or impact-loaded.
329-CDChoose it when strength drives the design.
329 Annealed vs 329-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.3 · Compressive Strength 540 MPa78.3 ksi · Shear Strength 430 MPa62.4 ksi · Fracture Toughness (K_IC) 100 MPa·√m91 ksi·√in · Hardness, Rockwell B 98 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 15.5 W/m·K9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.9 µm/m·K6.1 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Max Service Temperature (continuous) 290°C554 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V · Corrosion Resistance 72 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 30 / 100 · Weldability 45 / 100 · Castability 55 / 100 · Brazeability / Solderability 40 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 5.5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
329 Annealed vs 329-CD — frequently asked
Is 329-CD stronger than 329 Annealed?
Yes. 329-CD has a typical yield strength of 700 MPa (102 ksi) against 540 MPa (78.3 ksi) for 329 Annealed — about 30% more. Tensile strength is 860 MPa (125 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Annealed is the default 329 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 329 Annealed over 329-CD?
Pick 329 Annealed when the part is bent, formed or impact-loaded. Pick 329-CD when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 329 Annealed and 329-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.