Stainless Steel 310L NAG Annealed vs 310L NAG-CD
Stainless Steel · 310L NAG temper comparison
310L NAG Annealed and 310L NAG-CD are two conditions of the same stainless steel grade, 310L NAG: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 310L NAG-CD is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 305 MPa (44.2 ksi) for 310L NAG Annealed, about 84% more; tensile strength follows at 760 MPa (110 ksi) vs 620 MPa (89.9 ksi). In exchange, 310L NAG Annealed is the more ductile: elongation 48% versus 25% for 310L NAG-CD, and 310L NAG-CD is harder (230 HB vs 165 HB). 310L NAG Annealed runs hotter in service (600°C vs 500°C continuous).
310L NAG AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
310L NAG-CDChoose it when strength drives the design.
310L NAG Annealed vs 310L NAG-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi · Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.5 g/cm³0.27 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 13 W/m·K7.5 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15.7 µm/m·K8.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.9 % IACS · Electrical Resistivity 9×10⁻⁷ Ω·m35.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.08 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
310L NAG Annealed vs 310L NAG-CD — frequently asked
Is 310L NAG-CD stronger than 310L NAG Annealed?
Yes. 310L NAG-CD has a typical yield strength of 560 MPa (81.2 ksi) against 305 MPa (44.2 ksi) for 310L NAG Annealed — about 84% more. Tensile strength is 760 MPa (110 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Annealed is the default 310L NAG condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 310L NAG Annealed or 310L NAG-CD?
310L NAG-CD. Its machinability rates fair (35/100) against poor (30/100) for 310L NAG Annealed; for welding the order is 310L NAG Annealed first (very good, 70/100) then 310L NAG-CD (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 310L NAG Annealed and 310L NAG-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.