Stainless Steel 20Cb-3 vs S33228
Stainless Steel · grade comparison
Stainless Steel 20Cb-3 and S33228 are both stainless steel grades. 20Cb-3 is the stronger of the two: yield strength 345 MPa (50 ksi) against 280 MPa (40.6 ksi) for S33228, about 23% more. S33228 is harder — 170 HB against 160 HB for 20Cb-3 — which matters for wear surfaces and threads. S33228 runs hotter in service (1,100°C vs 500°C continuous). On the shop floor, 20Cb-3 welds better (very good vs good), 20Cb-3 forms better (very good vs good), and 20Cb-3 sits in a lower cost tier (premium, $$$) than S33228 (high, $$$$).
20Cb-3Choose it when strength drives the design, or when it will be welded.
S33228Choose it when surface hardness matters, or when the part sees heat.
20Cb-3 vs S33228: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Yield Strength (0.2% offset)
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Tensile Strength (Ultimate) 620 MPa89.9 ksi · Elongation at Break 42%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Latent Heat of Fusion
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Castability
Same in both: Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 20Cb-3 | S33228 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Solution Annealed | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
20Cb-3 vs S33228 — frequently asked
Is 20Cb-3 stronger than S33228?
Yes. 20Cb-3 has a typical yield strength of 345 MPa (50 ksi) against 280 MPa (40.6 ksi) for S33228 — about 23% more. Tensile strength is 620 MPa (89.9 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 20Cb-3 or S33228?
20Cb-3 is the lower-cost material: it sits in the premium tier ($$$) while S33228 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 20Cb-3 or S33228?
20Cb-3, by a small margin. Both rate poor for machinability — 33/100 against 25/100 for S33228; for welding the order is 20Cb-3 first (very good, 75/100) then S33228 (good, 65/100).