Stainless Steel 20Cb-3 vs R20033
Stainless Steel · grade comparison
Stainless Steel 20Cb-3 and R20033 are both stainless steel grades. R20033 is the stronger of the two: yield strength 430 MPa (62.4 ksi) against 345 MPa (50 ksi) for 20Cb-3, about 25% more; tensile strength follows at 800 MPa (116 ksi) vs 620 MPa (89.9 ksi). R20033 is harder — 200 HB against 160 HB for 20Cb-3 — which matters for wear surfaces and threads. 20Cb-3 runs hotter in service (500°C vs 450°C continuous) and R20033 conducts electricity better (1.9 % IACS vs 1.6 % IACS). On the shop floor, 20Cb-3 forms better (very good vs good) and 20Cb-3 sits in a lower cost tier (premium, $$$) than R20033 (high, $$$$).
20Cb-3Choose it when the part sees heat, or when cost is the deciding factor.
R20033Choose it when strength drives the design, or when surface hardness matters.
20Cb-3 vs R20033: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Same in both: Poisson's Ratio 0.3 · Reduction in Area 60%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Latent Heat of Fusion
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 20Cb-3 | R20033 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Solution Annealed | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
20Cb-3 vs R20033 — frequently asked
Is R20033 stronger than 20Cb-3?
Yes. R20033 has a typical yield strength of 430 MPa (62.4 ksi) against 345 MPa (50 ksi) for 20Cb-3 — about 25% more. Tensile strength is 800 MPa (116 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 20Cb-3 or R20033?
20Cb-3 is the lower-cost material: it sits in the premium tier ($$$) while R20033 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 20Cb-3 or R20033?
20Cb-3, by a small margin. Both rate poor for machinability — 33/100 against 25/100 for R20033; for welding the order is 20Cb-3 first (very good, 75/100) then R20033 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20Cb-3 and R20033 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.