Stainless Steel 15Cr25Ti Annealed vs 15Cr25Ti-HR
Stainless Steel · 15Cr25Ti temper comparison
15Cr25Ti Annealed and 15Cr25Ti-HR are two conditions of the same stainless steel grade, 15Cr25Ti: Annealed versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 15Cr25Ti-HR is the stronger of the two: yield strength 360 MPa (52.2 ksi) against 300 MPa (43.5 ksi) for 15Cr25Ti Annealed, about 20% more; tensile strength follows at 560 MPa (81.2 ksi) vs 520 MPa (75.4 ksi). In exchange, 15Cr25Ti Annealed is the more ductile: elongation 22% versus 18% for 15Cr25Ti-HR, and 15Cr25Ti-HR is harder (205 HB vs 180 HB).
15Cr25Ti AnnealedChoose it when the part is bent, formed or impact-loaded.
15Cr25Ti-HRChoose it when strength drives the design.
15Cr25Ti Annealed vs 15Cr25Ti-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.6 g/cm³0.27 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 21 W/m·K12.1 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 1,050°C1,922 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.6 % IACS · Electrical Resistivity 6.7×10⁻⁷ Ω·m26.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 52 MJ/kg22,356 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 190 L/kg22.8 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
15Cr25Ti Annealed vs 15Cr25Ti-HR — frequently asked
Is 15Cr25Ti-HR stronger than 15Cr25Ti Annealed?
Yes. 15Cr25Ti-HR has a typical yield strength of 360 MPa (52.2 ksi) against 300 MPa (43.5 ksi) for 15Cr25Ti Annealed — about 20% more. Tensile strength is 560 MPa (81.2 ksi) vs 520 MPa (75.4 ksi).
Which condition does FabDigit quote by default, Annealed or HR?
Annealed is the default 15Cr25Ti condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 15Cr25Ti Annealed over 15Cr25Ti-HR?
Pick 15Cr25Ti Annealed when the part is bent, formed or impact-loaded. Pick 15Cr25Ti-HR when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 15Cr25Ti Annealed and 15Cr25Ti-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.