Stainless Steel 1.4983 AT+STAB vs 1.4983-CD
Stainless Steel · 1.4983 temper comparison
1.4983 AT+STAB and 1.4983-CD are two conditions of the same stainless steel grade, 1.4983: AT+STAB (+AT + stabilizing anneal) versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 1.4983-CD is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 280 MPa (40.6 ksi) for 1.4983 AT+STAB, about 61% more; tensile strength follows at 700 MPa (102 ksi) vs 590 MPa (85.6 ksi). In exchange, 1.4983 AT+STAB is the more ductile: elongation 38% versus 25% for 1.4983-CD, and 1.4983-CD is harder (220 HB vs 175 HB). 1.4983 AT+STAB runs hotter in service (650°C vs 550°C continuous).
1.4983 AT+STABChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4983-CDChoose it when strength drives the design.
1.4983 AT+STAB vs 1.4983-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 166 GPa24.1 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,385°C2,525 °F · Liquidus Temperature 1,430°C2,606 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16 µm/m·K8.9 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.3 % IACS · Electrical Resistivity 7.5×10⁻⁷ Ω·m29.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4983 AT+STAB vs 1.4983-CD — frequently asked
Is 1.4983-CD stronger than 1.4983 AT+STAB?
Yes. 1.4983-CD has a typical yield strength of 450 MPa (65.3 ksi) against 280 MPa (40.6 ksi) for 1.4983 AT+STAB — about 61% more. Tensile strength is 700 MPa (102 ksi) vs 590 MPa (85.6 ksi).
Which condition does FabDigit quote by default, AT+STAB or CD?
AT is the default 1.4983 condition in the FabDigit quote flow (neither AT+STAB nor CD). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4983 AT+STAB or 1.4983-CD?
1.4983-CD. Its machinability rates fair (38/100) against poor (33/100) for 1.4983 AT+STAB; for welding the order is 1.4983 AT+STAB first (good, 65/100) then 1.4983-CD (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4983 AT+STAB and 1.4983-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.