Stainless Steel 1.4935 +A vs 1.4935 +QT700
Stainless Steel · 1.4935 temper comparison
1.4935 +A and 1.4935 +QT700 are two conditions of the same stainless steel grade, 1.4935: +A (annealed) versus +QT700 (quenched and tempered, Rm 700–850 MPa class). The chemistry is identical, so every difference below comes from the condition. 1.4935 +QT700 is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for 1.4935 +A, about 17% more; tensile strength follows at 770 MPa (112 ksi) vs 720 MPa (104 ksi). In exchange, 1.4935 +A is the more ductile: elongation 20% versus 18% for 1.4935 +QT700, and 1.4935 +QT700 is harder (22 HRC vs 20 HRC). 1.4935 +QT700 runs hotter in service (600°C vs 400°C continuous).
1.4935 +AChoose it when the part is bent, formed or impact-loaded.
1.4935 +QT700Choose it when strength drives the design, or when the part sees heat.
1.4935 +A vs 1.4935 +QT700: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 216 GPa31.3 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3 · Charpy V-Notch Impact (RT) 45 J33.2 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 40 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 48 MJ/kg20,636 BTU/lb · Embodied Carbon (primary production) 3.2 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4935 +A vs 1.4935 +QT700 — frequently asked
Is 1.4935 +QT700 stronger than 1.4935 +A?
Yes. 1.4935 +QT700 has a typical yield strength of 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for 1.4935 +A — about 17% more. Tensile strength is 770 MPa (112 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, +A or +QT700?
+QT800 is the default 1.4935 condition in the FabDigit quote flow (neither +A nor +QT700). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1.4935 +A over 1.4935 +QT700?
Pick 1.4935 +A when the part is bent, formed or impact-loaded. Pick 1.4935 +QT700 when strength drives the design, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4935 +A and 1.4935 +QT700 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.