Stainless Steel 1.4848 vs ZG1Cr18Ni12Mo2Ti
Stainless Steel · grade comparison
Stainless Steel 1.4848 and ZG1Cr18Ni12Mo2Ti are both stainless steel grades. 1.4848 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 245 MPa (35.5 ksi) for ZG1Cr18Ni12Mo2Ti, about 14% more. In exchange, ZG1Cr18Ni12Mo2Ti is the more ductile: elongation 38% versus 14% for 1.4848, and 1.4848 is harder (190 HB vs 160 HB). 1.4848 runs hotter in service (1,100°C vs 700°C continuous) and ZG1Cr18Ni12Mo2Ti conducts electricity better (2.3 % IACS vs 1.9 % IACS). On the shop floor, ZG1Cr18Ni12Mo2Ti welds better (very good vs fair).
1.4848Choose it when strength drives the design, or when the part sees heat.
ZG1Cr18Ni12Mo2TiChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
1.4848 vs ZG1Cr18Ni12Mo2Ti: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Same in both: Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 4.6 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4848 | ZG1Cr18Ni12Mo2Ti |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4848 vs ZG1Cr18Ni12Mo2Ti — frequently asked
Is 1.4848 stronger than ZG1Cr18Ni12Mo2Ti?
Yes. 1.4848 has a typical yield strength of 280 MPa (40.6 ksi) against 245 MPa (35.5 ksi) for ZG1Cr18Ni12Mo2Ti — about 14% more. Tensile strength is 530 MPa (76.9 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, 1.4848 or ZG1Cr18Ni12Mo2Ti?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4848 or ZG1Cr18Ni12Mo2Ti?
ZG1Cr18Ni12Mo2Ti, by a small margin. Both rate poor for machinability — 33/100 against 25/100 for 1.4848; for welding the order is ZG1Cr18Ni12Mo2Ti first (very good, 78/100) then 1.4848 (fair, 45/100).