Stainless Steel 1.4848 vs 1.4857
Stainless Steel · grade comparison
Stainless Steel 1.4848 and 1.4857 are both stainless steel grades. 1.4848 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 250 MPa (36.3 ksi) for 1.4857, about 12% more; tensile strength follows at 530 MPa (76.9 ksi) vs 450 MPa (65.3 ksi). 1.4848 is the more ductile: elongation 14% versus 10% for 1.4857. 1.4848 is stiffer (185 GPa vs 175 GPa) and 1.4848 conducts electricity better (1.9 % IACS vs 1.7 % IACS). On the shop floor, 1.4848 sits in a lower cost tier (premium, $$$) than 1.4857 (high, $$$$).
1.4848Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1.4848 vs 1.4857: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Poisson's Ratio 0.29 · Charpy V-Notch Impact (RT) 12 J8.9 ft·lbf · Hardness, Brinell 190 HB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 1,100°C2,012 °F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Same in both: Machinability 25 / 100 · Weldability 45 / 100 · Brazeability / Solderability 30 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4848 | 1.4857 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4848 vs 1.4857 — frequently asked
Is 1.4848 stronger than 1.4857?
Yes. 1.4848 has a typical yield strength of 280 MPa (40.6 ksi) against 250 MPa (36.3 ksi) for 1.4857 — about 12% more. Tensile strength is 530 MPa (76.9 ksi) vs 450 MPa (65.3 ksi).
Which is cheaper, 1.4848 or 1.4857?
1.4848 is the lower-cost material: it sits in the premium tier ($$$) while 1.4857 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose 1.4848 over 1.4857?
Pick 1.4848 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4848 and 1.4857 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.