Stainless Steel 1.4749 Annealed vs 1.4749 AS-CAST
Stainless Steel · 1.4749 temper comparison
1.4749 Annealed and 1.4749 AS-CAST are two conditions of the same stainless steel grade, 1.4749: Annealed versus AS-CAST. The chemistry is identical, so every difference below comes from the condition. 1.4749 Annealed is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 250 MPa (36.3 ksi) for 1.4749 AS-CAST, about 32% more; tensile strength follows at 560 MPa (81.2 ksi) vs 450 MPa (65.3 ksi). 1.4749 Annealed is the more ductile: elongation 22% versus 1.5% for 1.4749 AS-CAST, and 1.4749 AS-CAST is harder (230 HB vs 170 HB). 1.4749 Annealed is stiffer (200 GPa vs 190 GPa). On the shop floor, 1.4749 Annealed machines more easily (fair vs poor) and 1.4749 Annealed welds better (30 vs 15 out of 100).
1.4749 AnnealedChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1.4749 Annealed vs 1.4749 AS-CAST: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.6 g/cm³0.27 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 1,100°C2,012 °F · Min Service Temperature 0°C32 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 50 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 48 MJ/kg20,636 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 150 L/kg18 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4749 Annealed vs 1.4749 AS-CAST — frequently asked
Is 1.4749 Annealed stronger than 1.4749 AS-CAST?
Yes. 1.4749 Annealed has a typical yield strength of 330 MPa (47.9 ksi) against 250 MPa (36.3 ksi) for 1.4749 AS-CAST — about 32% more. Tensile strength is 560 MPa (81.2 ksi) vs 450 MPa (65.3 ksi).
Which condition does FabDigit quote by default, Annealed or AS-CAST?
Annealed is the default 1.4749 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4749 Annealed or 1.4749 AS-CAST?
1.4749 Annealed. Its machinability rates fair (42/100) against poor (28/100) for 1.4749 AS-CAST; for welding the order is 1.4749 Annealed first (poor, 30/100) then 1.4749 AS-CAST (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4749 Annealed and 1.4749 AS-CAST side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.