Stainless Steel 1.4570 +AT vs 1.4570 +C800
Stainless Steel · 1.4570 temper comparison
1.4570 +AT and 1.4570 +C800 are two conditions of the same stainless steel grade, 1.4570: +AT (solution annealed) versus +C800 (cold worked to tensile class Rm ≥ 800 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4570 +C800 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 260 MPa (37.7 ksi) for 1.4570 +AT, about 138% more; tensile strength follows at 860 MPa (125 ksi) vs 600 MPa (87 ksi). In exchange, 1.4570 +AT is the more ductile: elongation 45% versus 13% for 1.4570 +C800, and 1.4570 +C800 is harder (260 HB vs 175 HB). 1.4570 +AT runs hotter in service (760°C vs 400°C continuous).
1.4570 +ATChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4570 +C800Choose it when strength drives the design.
1.4570 +AT vs 1.4570 +C800: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 193 GPa28 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.3×10⁻⁷ Ω·m28.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 72 / 100 · Machinability Rating (AISI 1212 = 100 %) 78% · Brazeability / Solderability 55 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 5 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4570 +AT vs 1.4570 +C800 — frequently asked
Is 1.4570 +C800 stronger than 1.4570 +AT?
Yes. 1.4570 +C800 has a typical yield strength of 620 MPa (89.9 ksi) against 260 MPa (37.7 ksi) for 1.4570 +AT — about 138% more. Tensile strength is 860 MPa (125 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, +AT or +C800?
+AT is the default 1.4570 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1.4570 +AT over 1.4570 +C800?
Pick 1.4570 +AT when the part is bent, formed or impact-loaded, or when the part sees heat. Pick 1.4570 +C800 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4570 +AT and 1.4570 +C800 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.