Stainless Steel 1.4565 vs 20Cb-3
Stainless Steel · grade comparison
Stainless Steel 1.4565 and 20Cb-3 are both stainless steel grades. 1.4565 is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 345 MPa (50 ksi) for 20Cb-3, about 33% more; tensile strength follows at 850 MPa (123 ksi) vs 620 MPa (89.9 ksi). 1.4565 is the more ductile: elongation 50% versus 42% for 20Cb-3, and 1.4565 is harder (220 HB vs 160 HB). 20Cb-3 runs hotter in service (500°C vs 450°C continuous) and 1.4565 conducts electricity better (1.9 % IACS vs 1.6 % IACS). On the shop floor, 20Cb-3 machines more easily (33 vs 22 out of 100), 20Cb-3 welds better (very good vs good), and 20Cb-3 sits in a lower cost tier (premium, $$$) than 1.4565 (high, $$$$).
1.4565Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
20Cb-3Choose it when the part sees heat, or when the part is machined in volume.
1.4565 vs 20Cb-3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Poisson's Ratio 0.3 · Reduction in Area 60% · Charpy V-Notch Impact (RT) 200 J148 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 3.1 mm²/s
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4565 | 20Cb-3 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Solution Annealed |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4565 vs 20Cb-3 — frequently asked
Is 1.4565 stronger than 20Cb-3?
Yes. 1.4565 has a typical yield strength of 460 MPa (66.7 ksi) against 345 MPa (50 ksi) for 20Cb-3 — about 33% more. Tensile strength is 850 MPa (123 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 1.4565 or 20Cb-3?
20Cb-3 is the lower-cost material: it sits in the premium tier ($$$) while 1.4565 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4565 or 20Cb-3?
20Cb-3, by a small margin. Both rate poor for machinability — 33/100 against 22/100 for 1.4565; for welding the order is 20Cb-3 first (very good, 75/100) then 1.4565 (good, 65/100).