Stainless Steel 1.4466-CD vs 1.4466 CR-1/4H
Stainless Steel · 1.4466 temper comparison
1.4466-CD and 1.4466 CR-1/4H are two conditions of the same stainless steel grade, 1.4466: CD (cold drawn) versus CR-1/4H (cold Rolled 1/4 Hard). The chemistry is identical, so every difference below comes from the condition. 1.4466 CR-1/4H is the stronger of the two: yield strength 600 MPa (87 ksi) against 550 MPa (79.8 ksi) for 1.4466-CD, about 9% more; tensile strength follows at 800 MPa (116 ksi) vs 750 MPa (109 ksi). In exchange, 1.4466-CD is the more ductile: elongation 25% versus 18% for 1.4466 CR-1/4H.
1.4466-CDChoose it when the part is bent, formed or impact-loaded.
1.4466 CR-1/4HChoose it when strength drives the design.
1.4466-CD vs 1.4466 CR-1/4H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 50% · Fracture Toughness (K_IC) 150 MPa·√m137 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,410°C2,570 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 12 W/m·K6.9 BTU/hr·ft·°F · Specific Heat Capacity 490 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15 µm/m·K8.3 µin/in·°F · Latent Heat of Fusion 280 J/g120 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.9 % IACS · Electrical Resistivity 9×10⁻⁷ Ω·m35.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 85 MJ/kg36,543 BTU/lb · Embodied Carbon (primary production) 6.2 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4466-CD vs 1.4466 CR-1/4H — frequently asked
Is 1.4466 CR-1/4H stronger than 1.4466-CD?
Yes. 1.4466 CR-1/4H has a typical yield strength of 600 MPa (87 ksi) against 550 MPa (79.8 ksi) for 1.4466-CD — about 9% more. Tensile strength is 800 MPa (116 ksi) vs 750 MPa (109 ksi).
Which condition does FabDigit quote by default, CD or CR-1/4H?
SA is the default 1.4466 condition in the FabDigit quote flow (neither CD nor CR-1/4H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4466-CD or 1.4466 CR-1/4H?
1.4466-CD, by a small margin. Both rate poor for machinability — 33/100 against 24/100 for 1.4466 CR-1/4H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4466-CD and 1.4466 CR-1/4H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.