Stainless Steel 1.4424 vs 2304
Stainless Steel · grade comparison
Stainless Steel 1.4424 and 2304 are both stainless steel grades. 1.4424 is the stronger of the two: yield strength 490 MPa (71.1 ksi) against 460 MPa (66.7 ksi) for 2304, about 7% more. 1.4424 is the more ductile: elongation 35% versus 30% for 2304.
1.4424Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
1.4424 vs 2304: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.75 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13 µm/m·K7.2 µin/in·°F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 55 / 100 · Castability 45 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Same in both: Specific Stiffness (E / density) 25.8 MN·m/kg · Thermal Diffusivity 4.3 mm²/s · Thermal Shock Resistance Index 4
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4424 | 2304 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Solution Annealed |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4424 vs 2304 — frequently asked
Is 1.4424 stronger than 2304?
Yes. 1.4424 has a typical yield strength of 490 MPa (71.1 ksi) against 460 MPa (66.7 ksi) for 2304 — about 7% more. Tensile strength is 700 MPa (102 ksi) vs 680 MPa (98.6 ksi).
Which is cheaper, 1.4424 or 2304?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4424 or 2304?
2304. Its machinability rates fair (35/100) against poor (30/100) for 1.4424.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4424 and 2304 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.