Stainless Steel 1.4419 +QT vs 1.4419 +QT 54HRC
Stainless Steel · 1.4419 temper comparison
1.4419 +QT and 1.4419 +QT 54HRC are two conditions of the same stainless steel grade, 1.4419: +QT (quenched and tempered) versus +QT 54HRC. The chemistry is identical, so every difference below comes from the condition. 1.4419 +QT 54HRC is the stronger of the two: yield strength 1,650 MPa (239 ksi) against 850 MPa (123 ksi) for 1.4419 +QT, about 94% more; tensile strength follows at 1,900 MPa (276 ksi) vs 1,050 MPa (152 ksi). In exchange, 1.4419 +QT is the more ductile: elongation 12% versus 2% for 1.4419 +QT 54HRC, and 1.4419 +QT is harder (310 HB vs 225 HB). 1.4419 +QT runs hotter in service (500°C vs 250°C continuous). On the shop floor, 1.4419 +QT machines more easily (poor vs not recommended).
1.4419 +QTChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4419 +QT 54HRCChoose it when strength drives the design.
1.4419 +QT vs 1.4419 +QT 54HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 500 MPa72.5 ksi · Hardness, Rockwell B 98 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 24 W/m·K13.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4419 +QT vs 1.4419 +QT 54HRC — frequently asked
Is 1.4419 +QT 54HRC stronger than 1.4419 +QT?
Yes. 1.4419 +QT 54HRC has a typical yield strength of 1,650 MPa (239 ksi) against 850 MPa (123 ksi) for 1.4419 +QT — about 94% more. Tensile strength is 1,900 MPa (276 ksi) vs 1,050 MPa (152 ksi).
Which condition does FabDigit quote by default, +QT or +QT 54HRC?
+A is the default 1.4419 condition in the FabDigit quote flow (neither +QT nor +QT 54HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4419 +QT or 1.4419 +QT 54HRC?
1.4419 +QT. Its machinability rates poor (28/100) against not recommended (8/100) for 1.4419 +QT 54HRC; for welding the order is 1.4419 +QT first (poor, 15/100) then 1.4419 +QT 54HRC (not recommended, 8/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4419 +QT and 1.4419 +QT 54HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.