Stainless Steel 1.4411-AC vs 1.4411-H
Stainless Steel · 1.4411 temper comparison
1.4411-AC and 1.4411-H are two conditions of the same stainless steel grade, 1.4411: AC (spheroidize annealed) versus H (hardened). The chemistry is identical, so every difference below comes from the condition. 1.4411-H is the stronger of the two: yield strength 950 MPa (138 ksi) against 850 MPa (123 ksi) for 1.4411-AC, about 12% more; tensile strength follows at 1,250 MPa (181 ksi) vs 1,150 MPa (167 ksi). In exchange, 1.4411-AC is the more ductile: elongation 8% versus 7% for 1.4411-H, and 1.4411-H is harder (420 HB vs 380 HB).
1.4411-ACChoose it when the part is bent, formed or impact-loaded.
1.4411-HChoose it when strength drives the design.
1.4411-AC vs 1.4411-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 250°C482 °F · Min Service Temperature -80°C-112 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 7.9×10⁻⁷ Ω·m31.1 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 70 / 100 · Brazeability / Solderability 35 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.2 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4411-AC vs 1.4411-H — frequently asked
Is 1.4411-H stronger than 1.4411-AC?
Yes. 1.4411-H has a typical yield strength of 950 MPa (138 ksi) against 850 MPa (123 ksi) for 1.4411-AC — about 12% more. Tensile strength is 1,250 MPa (181 ksi) vs 1,150 MPa (167 ksi).
Which condition does FabDigit quote by default, AC or H?
QT1 is the default 1.4411 condition in the FabDigit quote flow (neither AC nor H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 1.4411-AC or 1.4411-H?
1.4411-AC. Its weldability rates fair (40/100) against fair (35/100) for 1.4411-H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4411-AC and 1.4411-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.