Stainless Steel 1.4310 +AT vs 1.4310 +C800
Stainless Steel · 1.4310 temper comparison
1.4310 +AT and 1.4310 +C800 are two conditions of the same stainless steel grade, 1.4310: +AT (solution annealed) versus +C800 (cold rolled, Rm 800–1000 MPa). The chemistry is identical, so every difference below comes from the condition. 1.4310 +C800 is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 280 MPa (40.6 ksi) for 1.4310 +AT, about 104% more; tensile strength follows at 880 MPa (128 ksi) vs 700 MPa (102 ksi). In exchange, 1.4310 +AT is the more ductile: elongation 50% versus 18% for 1.4310 +C800, and 1.4310 +AT is harder (32 HRC vs 25 HRC). 1.4310 +AT runs hotter in service (800°C vs 300°C continuous).
1.4310 +ATChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4310 +C800Choose it when strength drives the design.
1.4310 +AT vs 1.4310 +C800: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Same in both: Density 7.9 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.3×10⁻⁷ Ω·m28.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 160 L/kg19.2 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4310 +AT vs 1.4310 +C800 — frequently asked
Is 1.4310 +C800 stronger than 1.4310 +AT?
Yes. 1.4310 +C800 has a typical yield strength of 570 MPa (82.7 ksi) against 280 MPa (40.6 ksi) for 1.4310 +AT — about 104% more. Tensile strength is 880 MPa (128 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, +AT or +C800?
+C1000 is the default 1.4310 condition in the FabDigit quote flow (neither +AT nor +C800). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4310 +AT or 1.4310 +C800?
1.4310 +AT. Its machinability rates fair (35/100) against poor (28/100) for 1.4310 +C800; for welding the order is 1.4310 +AT first (good, 60/100) then 1.4310 +C800 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4310 +AT and 1.4310 +C800 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.