Stainless Steel 1.4116 Cold Rolled vs 1.4116 H&T 50-52 HRC
Stainless Steel · 1.4116 temper comparison
1.4116 Cold Rolled and 1.4116 H&T 50-52 HRC are two conditions of the same stainless steel grade, 1.4116: Cold Rolled versus H&T 50-52 HRC (hardened & Tempered to 50–52 HRC). The chemistry is identical, so every difference below comes from the condition. 1.4116 H&T 50-52 HRC is the stronger of the two: yield strength 1,450 MPa (210 ksi) against 750 MPa (109 ksi) for 1.4116 Cold Rolled, about 93% more; tensile strength follows at 1,700 MPa (247 ksi) vs 950 MPa (138 ksi). In exchange, 1.4116 Cold Rolled is the more ductile: elongation 8% versus 4% for 1.4116 H&T 50-52 HRC, and 1.4116 Cold Rolled is harder (300 HB vs 240 HB). 1.4116 Cold Rolled runs hotter in service (300°C vs 250°C continuous).
1.4116 Cold RolledChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4116 H&T 50-52 HRCChoose it when strength drives the design.
1.4116 Cold Rolled vs 1.4116 H&T 50-52 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
1.4116 Cold Rolled1.4116 H&T 50-52 HRC
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Hardness, Rockwell B 99 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 2.9 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 100 L/kg12 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4116 Cold Rolled vs 1.4116 H&T 50-52 HRC — frequently asked
Is 1.4116 H&T 50-52 HRC stronger than 1.4116 Cold Rolled?
Yes. 1.4116 H&T 50-52 HRC has a typical yield strength of 1,450 MPa (210 ksi) against 750 MPa (109 ksi) for 1.4116 Cold Rolled — about 93% more. Tensile strength is 1,700 MPa (247 ksi) vs 950 MPa (138 ksi).
Which condition does FabDigit quote by default, Cold Rolled or H&T 50-52 HRC?
Annealed is the default 1.4116 condition in the FabDigit quote flow (neither Cold Rolled nor H&T 50-52 HRC). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4116 Cold Rolled or 1.4116 H&T 50-52 HRC?
1.4116 H&T 50-52 HRC, by a small margin. Both rate fair for machinability — 45/100 against 40/100 for 1.4116 Cold Rolled; for welding the order is 1.4116 H&T 50-52 HRC first (poor, 20/100) then 1.4116 Cold Rolled (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4116 Cold Rolled and 1.4116 H&T 50-52 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.