Stainless Steel 1.4028 +A vs 1.4028 H+T200
Stainless Steel · 1.4028 temper comparison
1.4028 +A and 1.4028 H+T200 are two conditions of the same stainless steel grade, 1.4028: +A (annealed) versus H+T200 (hardened 1000–1050 °C, tempered 180–250 °C). The chemistry is identical, so every difference below comes from the condition. 1.4028 H+T200 is the stronger of the two: yield strength 1,500 MPa (218 ksi) against 450 MPa (65.3 ksi) for 1.4028 +A, about 3.3 times as much; tensile strength follows at 1,800 MPa (261 ksi) vs 740 MPa (107 ksi). In exchange, 1.4028 +A is the more ductile: elongation 17% versus 3% for 1.4028 H+T200, and 1.4028 H+T200 is harder (53 HRC vs 15 HRC). 1.4028 +A runs hotter in service (500°C vs 200°C continuous). On the shop floor, 1.4028 +A machines more easily (fair vs not recommended) and 1.4028 +A welds better (poor vs not recommended).
1.4028 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4028 H+T200Choose it when strength drives the design.
1.4028 +A vs 1.4028 H+T200: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Hardness, Brinell 210 HB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.5×10⁻⁷ Ω·m21.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 45 / 100 · Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 48 MJ/kg20,636 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 110 L/kg13.2 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4028 +A vs 1.4028 H+T200 — frequently asked
Is 1.4028 H+T200 stronger than 1.4028 +A?
Yes. 1.4028 H+T200 has a typical yield strength of 1,500 MPa (218 ksi) against 450 MPa (65.3 ksi) for 1.4028 +A — about 3.3 times as much. Tensile strength is 1,800 MPa (261 ksi) vs 740 MPa (107 ksi).
Which condition does FabDigit quote by default, +A or H+T200?
+A is the default 1.4028 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4028 +A or 1.4028 H+T200?
1.4028 +A. Its machinability rates fair (50/100) against not recommended (12/100) for 1.4028 H+T200; for welding the order is 1.4028 +A first (poor, 25/100) then 1.4028 H+T200 (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4028 +A and 1.4028 H+T200 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.