Stainless Steel 1.4005 +A vs 1.4005 +C700
Stainless Steel · 1.4005 temper comparison
1.4005 +A and 1.4005 +C700 are two conditions of the same stainless steel grade, 1.4005: +A (annealed) versus +C700 (cold drawn / centreless ground bar). The chemistry is identical, so every difference below comes from the condition. 1.4005 +C700 is the stronger of the two: yield strength 585 MPa (84.8 ksi) against 320 MPa (46.4 ksi) for 1.4005 +A, about 83% more; tensile strength follows at 760 MPa (110 ksi) vs 550 MPa (79.8 ksi). In exchange, 1.4005 +A is the more ductile: elongation 25% versus 14% for 1.4005 +C700, and 1.4005 +C700 is harder (230 HB vs 175 HB).
1.4005 +AChoose it when the part is bent, formed or impact-loaded.
1.4005 +C700Choose it when strength drives the design.
1.4005 +A vs 1.4005 +C700: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 330 MPa47.9 ksi · Shear Strength 360 MPa52.2 ksi · Hardness, Rockwell B 88 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Max Service Temperature (continuous) 600°C1,112 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V · Corrosion Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 15 / 100 · Brazeability / Solderability 40 / 100 · Polishability 35 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 43 MJ/kg18,487 BTU/lb · Embodied Carbon (primary production) 3 kg CO₂/kg · Embodied Water 100 L/kg12 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4005 +A vs 1.4005 +C700 — frequently asked
Is 1.4005 +C700 stronger than 1.4005 +A?
Yes. 1.4005 +C700 has a typical yield strength of 585 MPa (84.8 ksi) against 320 MPa (46.4 ksi) for 1.4005 +A — about 83% more. Tensile strength is 760 MPa (110 ksi) vs 550 MPa (79.8 ksi).
Which condition does FabDigit quote by default, +A or +C700?
+A is the default 1.4005 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 1.4005 +A over 1.4005 +C700?
Pick 1.4005 +A when the part is bent, formed or impact-loaded. Pick 1.4005 +C700 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4005 +A and 1.4005 +C700 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.