Solder & Low-Melting Alloy Sn63Pb37E vs Sn63Pb37Sb
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy Sn63Pb37E and Sn63Pb37Sb are both solder & low-melting alloy grades. Sn63Pb37Sb is the stronger of the two: yield strength 38 MPa (5.51 ksi) against 30 MPa (4.35 ksi) for Sn63Pb37E, about 27% more; tensile strength follows at 58 MPa (8.41 ksi) vs 46 MPa (6.67 ksi). In exchange, Sn63Pb37E is the more ductile: elongation 40% versus 32% for Sn63Pb37Sb, and Sn63Pb37E is harder (17 HB vs 16 HB). Sn63Pb37Sb is stiffer (32 GPa vs 30 GPa).
Sn63Pb37EChoose it when the part is bent, formed or impact-loaded.
Sn63Pb37SbChoose it when strength drives the design.
Sn63Pb37E vs Sn63Pb37Sb: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Bulk Modulus 50 GPa7.3 Msi · Poisson's Ratio 0.4
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 8.4 g/cm³0.3 lb/in³ · Melting Point (Solidus) 183°C361 °F
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Thermal Conductivity 50 W/m·K28.9 BTU/hr·ft·°F · Latent Heat of Fusion 42 J/g18.1 BTU/lb · Max Service Temperature (continuous) 100°C212 °F · Min Service Temperature -55°C-67 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 11.5 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.5 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Same in both: Machinability 20 / 100 · Formability (cold) 90 / 100 · Castability 95 / 100 · Brazeability / Solderability 100 / 100 · Polishability 25 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 210 MJ/kg90,284 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Sn63Pb37E | Sn63Pb37Sb |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Sn63Pb37E vs Sn63Pb37Sb — frequently asked
Is Sn63Pb37Sb stronger than Sn63Pb37E?
Yes. Sn63Pb37Sb has a typical yield strength of 38 MPa (5.51 ksi) against 30 MPa (4.35 ksi) for Sn63Pb37E — about 27% more. Tensile strength is 58 MPa (8.41 ksi) vs 46 MPa (6.67 ksi).
Which is cheaper, Sn63Pb37E or Sn63Pb37Sb?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose Sn63Pb37E over Sn63Pb37Sb?
Pick Sn63Pb37E when the part is bent, formed or impact-loaded. Pick Sn63Pb37Sb when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Sn63Pb37E and Sn63Pb37Sb side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.