Refractory Metal Ta-10W-ANN vs Ta-10W-SR
Refractory Metal · Ta-10W temper comparison
Ta-10W-ANN and Ta-10W-SR are two conditions of the same refractory metal grade, Ta-10W: ANN (annealed) versus SR (stress relieved). The chemistry is identical, so every difference below comes from the condition. Ta-10W-SR is the stronger of the two: yield strength 720 MPa (104 ksi) against 550 MPa (79.8 ksi) for Ta-10W-ANN, about 31% more; tensile strength follows at 830 MPa (120 ksi) vs 690 MPa (100 ksi). In exchange, Ta-10W-ANN is the more ductile: elongation 25% versus 15% for Ta-10W-SR, and Ta-10W-SR is harder (270 HB vs 225 HB).
Ta-10W-ANNChoose it when the part is bent, formed or impact-loaded.
Ta-10W-SRChoose it when strength drives the design.
Ta-10W-ANN vs Ta-10W-SR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 200 GPa29 Msi · Poisson's Ratio 0.33 · Hardness, Rockwell B 97 HRB
Physical
Density and transition temperatures.
Same in both: Density 16.8 g/cm³0.61 lb/in³ · Melting Point (Solidus) 3,030°C5,486 °F · Liquidus Temperature 3,080°C5,576 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 145 J/kg·K0.03 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 6.5 µm/m·K3.6 µin/in·°F · Latent Heat of Fusion 185 J/g79.5 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 95 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 15 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 3,600 MJ/kg1,547,723 BTU/lb · Embodied Carbon (primary production) 220 kg CO₂/kg · Embodied Water 2,500 L/kg300 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Ta-10W-ANN vs Ta-10W-SR — frequently asked
Is Ta-10W-SR stronger than Ta-10W-ANN?
Yes. Ta-10W-SR has a typical yield strength of 720 MPa (104 ksi) against 550 MPa (79.8 ksi) for Ta-10W-ANN — about 31% more. Tensile strength is 830 MPa (120 ksi) vs 690 MPa (100 ksi).
Which condition does FabDigit quote by default, ANN or SR?
ANN is the default Ta-10W condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Ta-10W-ANN or Ta-10W-SR?
Ta-10W-ANN. Its weldability rates very good (70/100) against good (65/100) for Ta-10W-SR.