Refractory Metal Pure Ta As Rolled vs Pure Ta R05200 PM
Refractory Metal · Pure Ta temper comparison
Pure Ta As Rolled and Pure Ta R05200 PM are two conditions of the same refractory metal grade, Pure Ta: As Rolled (hot rolled) versus R05200 PM (R05200). The chemistry is identical, so every difference below comes from the condition. Pure Ta As Rolled is the stronger of the two: yield strength 390 MPa (56.6 ksi) against 180 MPa (26.1 ksi) for Pure Ta R05200 PM, about 117% more; tensile strength follows at 450 MPa (65.3 ksi) vs 260 MPa (37.7 ksi). In exchange, Pure Ta R05200 PM is the more ductile: elongation 35% versus 8% for Pure Ta As Rolled, and Pure Ta R05200 PM is harder (100 HB vs 95 HB). Pure Ta R05200 PM runs hotter in service (300°C vs 250°C continuous).
Pure Ta As RolledChoose it when strength drives the design.
Pure Ta R05200 PMChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Pure Ta As Rolled vs Pure Ta R05200 PM: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Pure Ta As RolledPure Ta R05200 PM
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 69 GPa10 Msi · Bulk Modulus 200 GPa29 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 16.6 g/cm³0.6 lb/in³ · Melting Point (Solidus) 2,996°C5,425 °F · Liquidus Temperature 2,996°C5,425 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 140 J/kg·K0.03 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 6.5 µm/m·K3.6 µin/in·°F · Latent Heat of Fusion 202 J/g86.8 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Castability 10 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 4,200 MJ/kg1,805,677 BTU/lb · Embodied Carbon (primary production) 260 kg CO₂/kg · Embodied Water 700 L/kg83.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Pure Ta As Rolled vs Pure Ta R05200 PM — frequently asked
Is Pure Ta As Rolled stronger than Pure Ta R05200 PM?
Yes. Pure Ta As Rolled has a typical yield strength of 390 MPa (56.6 ksi) against 180 MPa (26.1 ksi) for Pure Ta R05200 PM — about 117% more. Tensile strength is 450 MPa (65.3 ksi) vs 260 MPa (37.7 ksi).
Which condition does FabDigit quote by default, As Rolled or R05200 PM?
Vacuum Annealed is the default Pure Ta condition in the FabDigit quote flow (neither As Rolled nor R05200 PM). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Pure Ta As Rolled or Pure Ta R05200 PM?
Pure Ta As Rolled, by a small margin. Both rate poor for machinability — 32/100 against 25/100 for Pure Ta R05200 PM; for welding the order is Pure Ta As Rolled first (good, 65/100) then Pure Ta R05200 PM (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pure Ta As Rolled and Pure Ta R05200 PM side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.